Polymide CoPa (Nylon)

Note:

1. PolyMide CoPa can be abrasive to brass nozzles if used extensively, manufacturer recommends using a hardened nozzle.
2. It is a Nylon material and his highly susceptible to moisture absorption. Store in dry environment.
3. Drying settings: 100 ^oC for 8 hours
4. Annealing settings: 80 ^oC for 6 hours

Manufacturer Recommended Print Settings

Nozzle Temperature: 250˚C – 270˚C

Printing Speed: 30mm/s – 60mm/s

Bed Temperature: 25˚C – 50˚C

Bed Surface: Glass with glue

Cooling Fan: OFF

 Mechanical Properties

Young’s Modulus: 2223 ± 199 Mpa

Tensile Strength: 66.2 ± 0.9 Mpa

Bending Strength: 97.0 ± 1.1 Mpa

Charpy Impact Strength: 9.6 ± 1.4 kJ/m2

 Thermal Properties

Glass Transition Temperature: 67˚C

Vicat Softening Temperature: 180˚C

Melting Temperature:190˚C